Two Fe-Zr-B-Cu Nanocrystalline Magnetic Alloys Produced by Mechanical Alloying Technique
Fe-rich soft magnetic alloys are candidates for applications as magnetic sensors and actuators. Spring magnets can be obtained when these alloys are added to hard magnetic compounds. In this work, two nanocrystalline Fe-Zr-B-Cu alloys are produced by mechanical alloying, MA. The increase in boron co...
| Autores: | , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2023 |
| País: | España |
| Recursos: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositorio: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:10256/25440 |
| Acesso em linha: | http://hdl.handle.net/10256/25440 |
| Access Level: | acceso abierto |
| Palavra-chave: | Aliatges Alloys Aliatge mecànic Mechanical alloying |
| Resumo: | Fe-rich soft magnetic alloys are candidates for applications as magnetic sensors and actuators. Spring magnets can be obtained when these alloys are added to hard magnetic compounds. In this work, two nanocrystalline Fe-Zr-B-Cu alloys are produced by mechanical alloying, MA. The increase in boron content favours the reduction of the crystalline size. Thermal analysis (by differential scanning calorimetry) shows that, in the temperature range compressed between 450 and 650 K, wide exothermic processes take place, which are associated with the relaxation of the tensions of the alloys produced by MA. At high temperatures, a main crystallisation peak is found. A Kissinger and an isoconversional method were used to determine the apparent activation of the exothermic processes. The values are compared with those found in the scientific literature. Likewise, adapted thermogravimetry allowed for the determination of the Curie temperature. The functional response has been analysed by hysteresis loop cycles. According to the composition, the decrease of the Fe/B ratio diminishes the soft magnetic behaviour. |
|---|