Fe-X-B-Cu (X = Nb, NiZr) Alloys Produced by Mechanical Alloying: Influence of Milling Device
In this work, we analyze the influence of the milling device in the microstructural evolution of two Fe-X-B-Cu (X = Nb, NiZr) alloys produced by mechanical alloying (MA). The two milling devices are a planetary mil (P7) and a shaker mill (SPEX 8000). Microstructural analysis by X-ray diffraction det...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2021 |
| País: | España |
| Institución: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositorio: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:10256/19381 |
| Acceso en línea: | http://hdl.handle.net/10256/19381 |
| Access Level: | acceso abierto |
| Palabra clave: | Aliatge mecànic Mechanical alloying |
| Sumario: | In this work, we analyze the influence of the milling device in the microstructural evolution of two Fe-X-B-Cu (X = Nb, NiZr) alloys produced by mechanical alloying (MA). The two milling devices are a planetary mil (P7) and a shaker mill (SPEX 8000). Microstructural analysis by X-ray diffraction detects the formation of a Fe rich solid solution. In the Fe-Nb-B-Cu alloy produced in the shaker mill also appears a Nb(B) minor phase, whereas in the Fe-NiZr-B-Cu alloy produced in the planetary mill, a minor disordered phase is formed. The comparative study regarding the energy transferred per unit of time in both devices determines that the shaker mill is more energetic. This fact explains that in the Fe-Nb-B-Cu alloy, Nb has not been introduced in the main Fe rich phase, whereas in the Fe-NiZr-B-Cu alloy milled in the shaker mill was formed the highly disordered phase. With regard to thermal analysis, the values of the apparent activation energies of the main crystallization process (above 200 kJ/mol) correspond to the crystalline growth of the nanocrystalline Fe rich phase |
|---|