Preparation and characterization of films extruded of Polyethylene/Chitosan modified with Poly(lactic acid)
The use of mixtures of synthetic and natural polymers is a potential option to reduce the pollution by plastic waste. In this work, the method for the chemical modification of chitosan with poly(lactic acid) was developed; then, the preparation of films of blends of polyethylene and chitosan-poly(la...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2015 |
| País: | México |
| Institución: | Centro de Investigación Científica de Yucatán |
| Repositorio: | Repositorio Institucional CICY |
| Idioma: | inglés |
| OAI Identifier: | oai:cicy.repositorioinstitucional.mx:1003/1597 |
| Acceso en línea: | http://cicy.repositorioinstitucional.mx/jspui/handle/1003/1597 |
| Access Level: | acceso abierto |
| Palabra clave: | info:eu-repo/classification/Autores/POLYETHYLENE info:eu-repo/classification/Autores/CHITOSAN info:eu-repo/classification/Autores/POLY(LACTIC ACID) info:eu-repo/classification/Autores/MALEIC ANHYDRIDE info:eu-repo/classification/Autores/EXTRUSION info:eu-repo/classification/cti/7 info:eu-repo/classification/cti/33 info:eu-repo/classification/cti/3312 info:eu-repo/classification/cti/331208 |
| Sumario: | The use of mixtures of synthetic and natural polymers is a potential option to reduce the pollution by plastic waste. In this work, the method for the chemical modification of chitosan with poly(lactic acid) was developed; then, the preparation of films of blends of polyethylene and chitosan-poly(lactic acid) produced by an extrusion method using polyethylene-graft maleic anhydride as a compatibilizer. It was possible to obtain films with a maximum content of 20 wt% and 30 wt%, chitosan, with and without compatibilizer, respectively. Scanning electron microscope (SEM) analysis showed a homogeneous surface on all films. The addition of the compatibilizer had a significant effect on the mechanical properties of the films, such as an increase in Young’s modulus and a decrease in the elongation at break; additionally, the compatibilizer promotes thermal degradation in a single step and gives the film a slight increase in thermal resistance. These results are attributed to an improved interaction in the interface of polyethylene and chitosan-poly(lactic acid), promoted by the compatibilizer. |
|---|