Microstructural influence on tolerance to corrosion-induced damage in hardmetals
The influence of the microstructure on the tolerance of WC-Co cemented carbides to corrosion damage was studied by using residual strength as the critical design parameter. In doing so, samples were immersed in synthetic mine water solution for different times, and changes induced by corrosion expos...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2016 |
| País: | España |
| Institución: | Universitat Politècnica de Catalunya (UPC) |
| Repositorio: | UPCommons. Portal del coneixement obert de la UPC |
| Idioma: | inglés |
| OAI Identifier: | oai:upcommons.upc.edu:2117/101243 |
| Acceso en línea: | https://hdl.handle.net/2117/101243 https://dx.doi.org/10.1016/j.matdes.2016.08.066 |
| Access Level: | acceso abierto |
| Palabra clave: | Strength of materials Carbides Cobalt Cemented carbides Corrosion Fracture 3D FIB/FESEM tomography Resistència de materials Metalls Carburs Àrees temàtiques de la UPC::Enginyeria dels materials |
| Sumario: | The influence of the microstructure on the tolerance of WC-Co cemented carbides to corrosion damage was studied by using residual strength as the critical design parameter. In doing so, samples were immersed in synthetic mine water solution for different times, and changes induced by corrosion exposure were assessed. A detailed 3D FIB/FESEM tomography characterization of corrosion damage-microstructure interactions is included. Results reveal that corrosion damage may result in relevant strength degradation on the basis of stress rising effects associated with the formation of surface corrosion pits. Thus, as immersion time increases strength gradually decreases. Fractographic examination reveals the formation of semi-elliptical and sharp corrosion pits for studied medium- and ultrafine-sized cemented carbides, respectively. The latter has a much more pronounced stress rising effect, and consequently higher strength losses were determined for ultrafine grades. Corrosion process consists of a selective attack of the binder that is dissolved in the corrosive media. Initially, it is located at centres of binder pools and as exposure time in the media increases, corrosion evolves consuming the rest of the pools which finally leaves an unsupported WC grain skeleton at the surface. |
|---|