New catalysts based on reduced graphene oxide for hydrogen production from ammonia decomposition
Promising and highly novel catalysts based on ruthenium (Ru) supported on reduced graphene oxide were synthesized, characterized and tested for COx-free hydrogen generation by catalytic ammonia decomposition. Metal loading and amount of a pre-reducing agent clearly affect the catalytic properties of...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2022 |
| País: | España |
| Institución: | Universidad de Castilla-La Mancha |
| Repositorio: | RUIdeRA. Repositorio Institucional de la UCLM |
| OAI Identifier: | oai:ruidera.uclm.es:10578/29868 |
| Acceso en línea: | https://hdl.handle.net/10578/29868 |
| Access Level: | acceso abierto |
| Palabra clave: | Ammonia decomposition Ruthenium Reduced graphene oxide Hydrogen production Descomposición de amoníaco Rutenio Óxido de grafeno reducido Producción de hidrógeno |
| Sumario: | Promising and highly novel catalysts based on ruthenium (Ru) supported on reduced graphene oxide were synthesized, characterized and tested for COx-free hydrogen generation by catalytic ammonia decomposition. Metal loading and amount of a pre-reducing agent clearly affect the catalytic properties of the final catalysts. A Ru loading higher than 2.5 wt% resulted in Ru particles of size higher than 5 nm, which were agglomerated, thus decreasing the amount of the most active sites (B5 type-sites) and therefore the ammonia conversion. Additionally, a graphene oxide (GO) hydrothermal pre-reduction with 2-chloroethylamine hydrochloride, led materials with a more ordered structure which is associated with a good electronic conductivity and, higher basicity. Optimal catalytic activity is achieved using a reducing agent/GO ratio of 5/3 (wt/wt) and a Ru loading of 2.5 wt%. Thus, 2.5Ru/10C-rGO catalyst resulted in excellent hydrogen (H2) production from ammonia decomposition, with an ammonia conversion close to 96% and hydrogen production rate of 9.1 mmolH2 gcat−1 min−1 at 400 °C. Reduced graphene oxide proved to be a suitable support in the development of nanosized Ru catalysts being the optimal one highly active in COx-free hydrogen generation during more than 60 h of reaction, providing virtuous stability. |
|---|