Structural, Mössbauer and magnetic study of (Mn0.2Co0.2Ni0.2Cu0.2X0.2)Fe2O4 (X=Fe, Mg) spinel high-entropy oxides fabricated via reactive flash sintering
Herein, it is reported the concomitant synthesis and sintering in a single step of (Mn0.2Co0.2Ni0.2Cu0.2X0.2)Fe2O4 (X=Fe, Mg), a spinel-structured high-entropy oxides, by the reactive flash sintering technique. A single phase, identified with a spinel crystal structure Fd3̅m, was obtained in just 30...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2024 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/382993 |
| Acceso en línea: | http://hdl.handle.net/10261/382993 https://api.elsevier.com/content/abstract/scopus_id/85196948537 |
| Access Level: | acceso abierto |
| Palabra clave: | High entropy oxides Magnetic properties Mössbauer spectroscopy Reactive flash sintering Soft magnetic materials |
| Sumario: | Herein, it is reported the concomitant synthesis and sintering in a single step of (Mn0.2Co0.2Ni0.2Cu0.2X0.2)Fe2O4 (X=Fe, Mg), a spinel-structured high-entropy oxides, by the reactive flash sintering technique. A single phase, identified with a spinel crystal structure Fd3̅m, was obtained in just 30 min at a furnace temperature of 1173 K. The structural and magnetic properties of the prepared compounds were assessed by the combined use of various techniques, aiming to understand the correlations between functional properties and crystal structure. Characteristic features of the Mössbauer spectra prove the existence of different nonequivalent Fe environments. Both compositions display soft magnetic behavior, characterized by low coercive fields and saturation magnetization reached at low fields. Thus, the substitution of nonmagnetic Mg2+ for magnetic Fe2+ results in a decrease in magnetic parameters due to the weakening of the super-exchange interaction among the magnetic moments. |
|---|