GaSb/Mn multilayers structures fabricated by DC magnetron sputtering: Interface feature and nano-scale surface topography
The multilayer structure is a well-studied architecture for electronic and optoelectronic applications and more recently in spintronic devices. In this work, we present the structural, morphological, topographical, and magnetic properties of GaSb/Mn multilayers deposited via DC magnetron sputtering...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2022 |
| País: | España |
| Institución: | Universidad Autónoma de Madrid |
| Repositorio: | Biblos-e Archivo. Repositorio Institucional de la UAM |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.uam.es:10486/707193 |
| Acceso en línea: | http://hdl.handle.net/10486/707193 https://dx.doi.org/10.1007/s10854-022-07965-9 |
| Access Level: | acceso abierto |
| Palabra clave: | GaSb/Mn multilayers Multilayer structure Electronic applications Spintronic devices Física |
| Sumario: | The multilayer structure is a well-studied architecture for electronic and optoelectronic applications and more recently in spintronic devices. In this work, we present the structural, morphological, topographical, and magnetic properties of GaSb/Mn multilayers deposited via DC magnetron sputtering at room temperature and 423 K. Raman measurements evidence the formation of p-type GaSb layers with a contribution of electrons in the multilayer due to the neighboring Mn layer and the formation of effective interlayers. HR-SEM measurements show the multilayer architecture with columnar microstructure in the layer’s formation, while AFM micrographs allowed observing the changes in grain sizes (between 129 and 187 nm) and roughness (between 1.47 nm and 6.28 nm) with increasing number of layers. The formation of the interlayers between the GaSb and Mn layer was assayed in-depth spectroscopically via Rutherford backscattering studies. These interlayers were associated with diffusion processes during deposition and contributed to the magnetic behavior of multilayers. A ferromagnetic-like behavior was observed in the multilayers |
|---|