Time- and space-resolved dynamics of melting, ablation, and solidification phenomena induced by femtosecond laser pulses in germanium
Femtosecond time-resolved microscopy has been used to analyze the structural transformation dynamics (melting, ablation, and solidification phenomena) induced by intense 130 fs laser pulses in single-crystalline (100)-germanium wafers on a time scale from ∼100 fs up to 10 ns. Complementary informati...
| Autores: | , , , |
|---|---|
| Tipo de documento: | artigo |
| Data de publicação: | 2006 |
| País: | España |
| Recursos: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositório: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/54145 |
| Acesso em linha: | http://hdl.handle.net/10261/54145 |
| Access Level: | Acceso aberto |
| Resumo: | Femtosecond time-resolved microscopy has been used to analyze the structural transformation dynamics (melting, ablation, and solidification phenomena) induced by intense 130 fs laser pulses in single-crystalline (100)-germanium wafers on a time scale from ∼100 fs up to 10 ns. Complementary information on longer time scales (350 ps-1.4 μs) has been obtained by means of simultaneous streak camera and photodiode measurements of the sample surface reflectivity. In the ablative regime, transient surface reflectivity patterns are observed by fs microscopy on a ps to ns time scale as a consequence of the complex spatial density structure of the ablating material. Complementing point-probing streak camera measurements allow one to characterize the temporal evolution in real time up to 40 ns after the fs-laser pulse excitation. Fs microscopy reveals additional reflectivity patterns for fluences below the ablation threshold of the germanium. It is shown that these patterns are originating from the selective removal of the native oxide layer at the wafer surface within a certain fluence range. After solidification, and in contrast to other semiconductors, surface amorphization has not been observed in (100)-germanium upon femtosecond laser pulse irradiation in the studied fluence range. © 2006 The American Physical Society. |
|---|