Cu-Doped TiO<
[EN] Cu-doped TiO2 films were synthesized directly on FTO glass with a spin coating method. With a variation in copper amount, samples were prepared with 0%, 1%, 2%, 4% and 8% of dopant concentrations. Morphological and structural characterization of undoped and Cu-doped TiO2 samples were investigat...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2024 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/208384 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/208384 |
| Access Level: | acceso abierto |
| Palabra clave: | Titanium dioxide TiO2 nanoparticles Copper Cu doping Perovskite solar cells PSCs Electron transport layer ETL FISICA APLICADA |
| Sumario: | [EN] Cu-doped TiO2 films were synthesized directly on FTO glass with a spin coating method. With a variation in copper amount, samples were prepared with 0%, 1%, 2%, 4% and 8% of dopant concentrations. Morphological and structural characterization of undoped and Cu-doped TiO2 samples were investigated and the obtained results showed the small, spherical shapes of the nanoparticles forming a thin film on top of FTO glass and their preferred orientation of TiO2 anatase (101), which is the same for each sample. However, this peak exhibited a slight shift for the 2% sample, related to the inflation of the microstrain compared to the other samples. For the optical properties, the 4% sample displayed the highest transmittance whereas the 2% sample exhibited the lowest band gap energy of 2.96 eV. Moreover, the PL intensity seems to be at its highest for the 2% sample due to the present peaking defects in the structure, whereas the 8% sample shows a whole new signal that is related to copper oxide. These properties make this material a potential candidate to perform as an electron transport layer (ETL) in solar cells and enhance their power conversion efficiency. |
|---|