Antifouling Mortars for Underwater Restoration
This research has focused on the assessment of the compositional features and mechanical and antifouling performances of two different mortars formulated for an underwater setting, and which contain Mg(OH)2 as an antifouling agent. Regarding the mechanical characterization, the uniaxial compressive...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2022 |
| País: | España |
| Institución: | Universidad Complutense de Madrid (UCM) |
| Repositorio: | Docta Complutense |
| Idioma: | inglés |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/73317 |
| Acceso en línea: | https://hdl.handle.net/20.500.14352/73317 |
| Access Level: | acceso abierto |
| Palabra clave: | 666.971 magnesium hydroxide mortars submerged sites biofouling geomaterials restoration nanoparticles Petrología |
| Sumario: | This research has focused on the assessment of the compositional features and mechanical and antifouling performances of two different mortars formulated for an underwater setting, and which contain Mg(OH)2 as an antifouling agent. Regarding the mechanical characterization, the uniaxial compressive strength and flexural strength were measured. The composition of the materials was explored by differential thermal/thermogravimetric analysis (DTA-TG), X-ray diffraction analysis (XRPD), and scanning electronic microscopy (SEM) coupled with EDS microanalysis. The assessment of the biological colonization was evaluated with colorimetric analysis and image analysis. The results suggest that both mortars have good mechanical resistance once set underwater. Moreover, the adding of Mg(OH)2 improves the resistance toward biofouling; this was observed both in laboratory and sea-exposed specimens. |
|---|