Selective Aerobic Oxidation of Cumene to Cumene Hydroperoxide over Mono- and Bimetallic Trimesate Metal Organic Frameworks Prepared by a Facile Green Aqueous Synthesis
[EN] Co-Ni and Mn-Ni bimetallic trimesate MOFs prepared by a fast aqueous synthesis method are excellent and reusable catalysts for the selective aerobic oxidation of cumene to cumene hydroperoxide (CHP). Isolation of Co2+ (or Mn2+) in an inert Ni-BTC framework is a good strategy to optimize CHP sel...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2019 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/150627 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/150627 |
| Access Level: | acceso abierto |
| Palabra clave: | Aerobic cumene oxidation Bimetallic MOFs MOF catalysis Single-site catalysts Site isolation |
| Sumario: | [EN] Co-Ni and Mn-Ni bimetallic trimesate MOFs prepared by a fast aqueous synthesis method are excellent and reusable catalysts for the selective aerobic oxidation of cumene to cumene hydroperoxide (CHP). Isolation of Co2+ (or Mn2+) in an inert Ni-BTC framework is a good strategy to optimize CHP selectivity above 90%: since only Co2+ sites catalyze CHP decomposition, a drop of the CHP selectivity is observed as the cobalt content in the bimetallic MOF increases. The statistical probability of having isolated Co2+ sites is calculated as a function of the total cobalt content of the bimetallic compound, assuming homogeneous distribution of Co2+ ions in the Ni-BTC framework and preferential occupation of terminal sites. Thus, in our best sample, with a Co:Ni ratio of 5:95, 73% of the total Co2+ ions are isolated so that CHP decomposition/overoxidation processes at the surface of the catalyst are not likely to occur before CHP desorption. This can explain the excellent CHP selectivity (91%) attained over this material. This "site isolation" effect is further supported by similar findings on Mn-Ni bimetallic compounds. |
|---|