Optical waveguides in LiTaO3 crystals fabricated by swift C5+ ion irradiation
We report on the optical waveguides, in both planar and ridge configurations, fabricated in LiTaO3 crystal by using carbon (C5+) ions irradiation at energy of 15 MeV. The planar waveguide was produced by direct irradiation of swift C5+ ions, whilst the ridge waveguides were manufactured by using fem...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2014 |
| País: | España |
| Institución: | Universidad de Salamanca (USAL) |
| Repositorio: | GREDOS. Repositorio Institucional de la Universidad de Salamanca |
| OAI Identifier: | oai:gredos.usal.es:10366/146839 |
| Acceso en línea: | http://hdl.handle.net/10366/146839 |
| Access Level: | acceso abierto |
| Palabra clave: | Ion irradiation LiTaO3 crystal Optical waveguide |
| Sumario: | We report on the optical waveguides, in both planar and ridge configurations, fabricated in LiTaO3 crystal by using carbon (C5+) ions irradiation at energy of 15 MeV. The planar waveguide was produced by direct irradiation of swift C5+ ions, whilst the ridge waveguides were manufactured by using femtosecond laser ablation of the planar layer. The reconstructed refractive index profile of the planar waveguide has showed a barrier-shaped distribution, and the near-field waveguide mode intensity distribution was in good agreement with the calculated modal profile. After thermal annealing at 260 °C in air, the propagation losses of both the planar and ridge waveguides were reduced to 10 dB/cm. |
|---|