Tuning green to red color in erbium niobate micro - and nanoparticles
Tetragonal Er0.5Nb0.5O2 and monoclinic ErNbO4 micro- and nanoparticles were prepared by the citrate sol–gel method and heat-treated at temperatures between 700 and 1600 °C. ErNbO4 revealed a spherical-shaped crystallite, whose size increased with heat treatment temperatures. To assess their optical...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2021 |
| País: | Brasil |
| Institución: | Universidade Federal do Ceará (UFC) |
| Repositorio: | Repositório Institucional da Universidade Federal do Ceará (UFC) |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.ufc.br:riufc/71868 |
| Acceso en línea: | https://doi.org/10.3390/ nano11030660 http://www.repositorio.ufc.br/handle/riufc/71868 |
| Access Level: | acceso abierto |
| Palabra clave: | Erbium niobate Sol-gel PL PLE TRPL Niobato de erbio |
| Sumario: | Tetragonal Er0.5Nb0.5O2 and monoclinic ErNbO4 micro- and nanoparticles were prepared by the citrate sol–gel method and heat-treated at temperatures between 700 and 1600 °C. ErNbO4 revealed a spherical-shaped crystallite, whose size increased with heat treatment temperatures. To assess their optical properties at room temperature (RT), a thorough spectroscopic study was conducted. RT photoluminescence (PL) spectroscopy revealed that Er3+ optical activation was achieved in all samples. The photoluminescence spectra show the green/yellow 2H11/2, 4S3/2→4I15/2 and red 4F9/2→4I15/2 intraionic transitions as the main visible recombination, with the number of the crystal field splitting Er3+ multiplets reflecting the ion site symmetry in the crystalline phases. PL excitation allows the identification of Er3+ high-energy excited multiplets as the preferential population paths of the emitting levels. Independently of the crystalline structure, the intensity ratio between the green/yellow and red intraionic transitions was found to be strongly sensitive to the excitation energy. After pumping the samples with a resonant excitation into the 4G11/2 excited multiplet, a green/yellow transition stronger than the red one was observed, whereas the reverse occurred for higher excitation photon energies. Thus, a controllable selective excited tunable green to red color was achieved, which endows new opportunities for photonic and optoelectronic applications. |
|---|