Synthesis and TL Characterization of Li2B4O7 Doped with Cooper and Manganese
Copper (Cu) and manganese (Mn) doped tissue equivalent Li2B4O7 were prepared by solid state sintering. The glow curves shows a high temperature peak at 222 °C for Li2B4O7:Cu and for Li2B4O7:Mn at 218 °C. Linear dose response is observed up to 140 Gy. With a thermal treatment at 125 °C, the first pea...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2013 |
| País: | Argentina |
| Institución: | Consejo Nacional de Investigaciones Científicas y Técnicas |
| Repositorio: | CONICET Digital (CONICET) |
| Idioma: | inglés |
| OAI Identifier: | oai:ri.conicet.gov.ar:11336/4570 |
| Acceso en línea: | http://hdl.handle.net/11336/4570 |
| Access Level: | acceso abierto |
| Palabra clave: | THERMOLUMINESCENCE DOSIMETERS RADIATION COPPER - MANGANESE https://purl.org/becyt/ford/1.3 https://purl.org/becyt/ford/1 |
| Sumario: | Copper (Cu) and manganese (Mn) doped tissue equivalent Li2B4O7 were prepared by solid state sintering. The glow curves shows a high temperature peak at 222 °C for Li2B4O7:Cu and for Li2B4O7:Mn at 218 °C. Linear dose response is observed up to 140 Gy. With a thermal treatment at 125 °C, the first peak of the phosphors doped with copper (95 °C) and manganese (90 °C) disappears and the main TL peaks remain isolated. The dose rate dependence was studied by exposing the samples at doses of 25 Gy and 250 Gy. At low dose it was observed that the Li2B4O7:Cu TL response has non-dependence on dose rate, and at higher dose was observed that there is a dependence of the TL response with the different dose rate |
|---|