Surface processes at a polymetallic (Mn-Fe-Pb) sulfide subject to cyanide leaching under sonication conditions and with an alkaline pretreatment: Understanding differences in silver extraction with X-ray photoelectron spectroscopy (XPS)
Leaching of polymetallic sulfides is often challenging due to the complexity of these systems. The main issues are related to the formation of surface by-products or to the presence of different metals that require a greater consumption of chemicals compared to that needed to extract the target meta...
| Autores: | , , , , , , , , , , |
|---|---|
| Formato: | artículo |
| Fecha de publicación: | 2021 |
| País: | Perú |
| Recursos: | Consejo Nacional de Ciencia Tecnología e Innovación |
| Repositorio: | CONCYTEC-Institucional |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.concytec.gob.pe:20.500.12390/2385 |
| Acesso em linha: | https://hdl.handle.net/20.500.12390/2385 https://doi.org/10.1016/j.hydromet.2020.105544 |
| Access Level: | acceso abierto |
| Palavra-chave: | XPS Cyanide Leaching Polymetallic Pretreatment Sonication Sulfide Surface analysis Ultrasound-assisted http://purl.org/pe-repo/ocde/ford#1.04.0 |
| Resumo: | Leaching of polymetallic sulfides is often challenging due to the complexity of these systems. The main issues are related to the formation of surface by-products or to the presence of different metals that require a greater consumption of chemicals compared to that needed to extract the target metal during leaching. This latter case is followed in the present work using X-ray photoelectron spectroscopy (XPS) during the leaching of a silver-containing polymetallic (Mn-Fe-Pb) sulfide under three different cyanidation procedures: (1) conventional leaching, (2) ultrasound-assisted leaching, and (3) leaching of a sample pretreated in alkaline media. In all cases, leaching results in the build-up of Pb compounds (oxides/hydroxides) on the surface of the minerals, suggesting a mechanism in which Pb is first leached by hydroxide and cyanide and later is re-adsorbed as an external layer on the minerals. On the other hand, the effect of each process on Mn was quite distinct: 1) Conventional leaching leads to the oxidation of the sulfide (pyrite) surface and a slight increase of surface Mn species; 2) Ultrasound-assisted leaching decreases surface Mn by dissolving oxidized species, which exposes fresh sulfide surfaces and increases Ag extraction; and 3) An alkaline pretreatment at high temperature exposed fresh sulfide surfaces and decreased the surface concentration of Mn. The fact that ultrasound-assisted leaching and leaching after an alkaline pretreatment allow for a higher Ag extraction (60% and 75% of total Ag, respectively, as opposed to the 25% extracted via conventional leaching), indicates that leaching is more efficient if the surface is not oxidized and if Mn is removed from the samples, either before or during leaching. © 2020 Elsevier B.V. |
|---|