Two step synthesis of TlBa2Ca2Cu3Ox films on Ag substrates by spray pyrolysis of metal-acetylacetonates
A two-step synthesis process was performed to obtain TlBa2Ca2Cu3Ox (Tl-1223) superconductor films. The synthesized films were obtained under different thallium diffusion conditions in a two-zone furnace precursor films were deposited at 550° C on silver substrates using the spray pyrolysis technique...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2008 |
| País: | México |
| Institución: | Instituto Politécnico Nacional |
| Repositorio: | Redalyc-IPN |
| OAI Identifier: | oai:redalyc.org:57016053007 |
| Acceso en línea: | https://www.redalyc.org/articulo.oa?id=57016053007 |
| Access Level: | acceso abierto |
| Palabra clave: | Física, Astronomía y Matemáticas thin films Superconductors spray pyrolysis |
| Sumario: | A two-step synthesis process was performed to obtain TlBa2Ca2Cu3Ox (Tl-1223) superconductor films. The synthesized films were obtained under different thallium diffusion conditions in a two-zone furnace precursor films were deposited at 550° C on silver substrates using the spray pyrolysis technique from acetylacetonates (2, 4-pentanedionates) as reagents. Second, a thallium diffusion process is carried out to incorporate Tl in the films. For this task Tl2O3 pellets, as a Tl source, were used at 750°C. Different oxygen flow rates at atmospheric pressure were used in order to get the thallous oxide p (Tl2O) partial pressure in the range of 6.9 x 10-4 to 6.1 x 10-2 atm. The Tl-1223 phase was obtained in all cases, though for a low p (Tl2O), the films presented the BaCuO2 phase mixed with the Tl-1223 one. Critical temperature (T C) values for these films were in the range of 90 to 102 K. |
|---|