The influence of texture on the reversible elastocaloric effect of a polycrystalline Ni50Mn32In16Cr2 alloy
"We have studied the correlation between the elastocaloric effect and the crystallographic direction where a uniaxial stress is applied in a textured polycrystalline Ni-Mn-In-Cr ferromagnetic shape memory alloy; this alloy displays martensitic transformation around room temperature and presents...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2018 |
| País: | México |
| Institución: | Instituto Potosino de Investigación Científica y Tecnológica |
| Repositorio: | Repositorio Institucional del IPICYT |
| OAI Identifier: | oai:ipicyt.repositorioinstitucional.mx:1010/1990 |
| Acceso en línea: | http://ipicyt.repositorioinstitucional.mx/jspui/handle/1010/1990 |
| Access Level: | acceso embargado |
| Palabra clave: | info:eu-repo/classification/Autor/Shape-memory alloys info:eu-repo/classification/Autor/Transformation info:eu-repo/classification/cti/1 info:eu-repo/classification/cti/22 |
| Sumario: | "We have studied the correlation between the elastocaloric effect and the crystallographic direction where a uniaxial stress is applied in a textured polycrystalline Ni-Mn-In-Cr ferromagnetic shape memory alloy; this alloy displays martensitic transformation around room temperature and presents an L2(1) cubic structure in the austenite phase. The texture in the material was induced by simple arc melting synthesis; using inverse pole figures, a favored grain growth was shown in the direction [001] perpendicular to the cooled surface. The elastocaloric effect was determined by direct measurements of the adiabatic temperature change (Delta T-ad(me)), while compressive stress was applied and released; hereby, it has been shown that it is possible to exploit the columnar growth texture in order to obtain a large and reversible elastocaloric effect. The reversible elastocaloric response was measured between 280 and 310K by applying moderate stresses of 50, 75, and 100 MPa in the [001], [111], and [011] directions. A strong interrelation was found in the cyclic Delta T-ad(me) values of -3.9, -2.0, and -1.3K after unloading a compressive stress of 100 MPa applied mainly in the [001], [111], and [011] directions, respectively." |
|---|