Optimizing the curie temperature of pseudo-binary RxR'2-xFe17 (R,R' = rare earth) for magnetic refrigeration
"Several pseudo-binary RxR2-x'Fe-17 alloys (with R = Y, Ce, Pr, Gd and Dy) were synthesized with rhombohedral Th2Zn17-type crystal structure determined from x-ray and neutron powder diffraction. The choice of compositions was done with the aim of tuning the Curie temperature (T-C) in the 2...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2014 |
| País: | México |
| Institución: | Instituto Potosino de Investigación Científica y Tecnológica |
| Repositorio: | Repositorio Institucional del IPICYT |
| OAI Identifier: | oai:ipicyt.repositorioinstitucional.mx:1010/1960 |
| Acceso en línea: | http://ipicyt.repositorioinstitucional.mx/jspui/handle/1010/1960 |
| Access Level: | acceso abierto |
| Palabra clave: | info:eu-repo/classification/cti/1 info:eu-repo/classification/cti/22 |
| Sumario: | "Several pseudo-binary RxR2-x'Fe-17 alloys (with R = Y, Ce, Pr, Gd and Dy) were synthesized with rhombohedral Th2Zn17-type crystal structure determined from x-ray and neutron powder diffraction. The choice of compositions was done with the aim of tuning the Curie temperature (T-C) in the 270 +/- 20 K temperature range, in order to obtain the maximum magneto-caloric effect around room temperature. The investigated compounds exhibit broad isothermal magnetic entropy changes, Delta S-M(T), with moderate values of the refrigerant capacity, even though the values of Delta S-M(Peak) are relatively low compared with those of the R2Fe17 compounds with R = Pr or Nd. The reduction on the Delta S-M(Peak) is explained in terms of the diminution in the saturation magnetization value. Furthermore, the Delta S-M(T) curves exhibit a similar caret-like behavior, suggesting that the magneto-caloric effect is mainly governed by the Fe-sublattice. A single master curve for Delta S-M/Delta S-M(Peak)(T) under different values of the magnetic field change are obtained for each compound by rescaling of the temperature axis." |
|---|