Recycled glass and Ce‐Doped‐Y3Al5O12 nanoparticles phosphor‐in‐glass for white light‐emitting diodes applications
A series of nanocomposites of recycled soda‐lime glass from a glass container and Y3Al5O12:Ce3+ (YAG:Ce) phosphor nanoparticles are fabricated by the two‐step low‐temperature co‐sintering technology. A transparent glass bottle from a commercial beverage is used as glass frit source and mixed with YA...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2020 |
| País: | México |
| Institución: | Universidad Autónoma de Ciudad Juárez |
| Repositorio: | Repositorio Institucional de la Universidad Autónoma de Ciudad Juárez |
| OAI Identifier: | oai:uacj.mx:oai:cathi.uacj.mx:20.500.11961ir-11922 |
| Acceso en línea: | https://doi.org/10.1002/pssa.202000226 |
| Access Level: | acceso abierto |
| Palabra clave: | nanoparticles recycled glass phosphor-in-glass photoluminescence WLEDs info:eu-repo/classification/cti/7 |
| Sumario: | A series of nanocomposites of recycled soda‐lime glass from a glass container and Y3Al5O12:Ce3+ (YAG:Ce) phosphor nanoparticles are fabricated by the two‐step low‐temperature co‐sintering technology. A transparent glass bottle from a commercial beverage is used as glass frit source and mixed with YAG:Ce nanoparticles. Afterward, the powders are pressed to obtain pellets with phosphor concentrations in the range of 2.5–15 wt%. The pellets are sintered at 800 and 900 °C. X‐ray diffraction (XRD) analysis shows that YAG:Ce nanoparticles are conserved even after sintering at 900 °C. The XRD analysis shows that YAG:Ce nanoparticles are conserved even after sintering at 900 °C. The emission spectra of the Ce3+ ions of yttrium aluminum garnet (YAG) nanoparticles combined with the transmitted blue light exhibit color tuning related to the phosphor concentration and the sintering temperature. A tonality shift from cold‐white light toward yellowish‐green region is observed according to the estimated CIE 1931 chromaticity. Thus, recycled glass from a commercial glass container and YAG:Ce nanoparticles phosphor‐in‐glass (PiG) can be an eco‐friendly and low‐cost alternative as color converters. |
|---|