Characterization and Modification of Red Mud and Ferrosilicomanganese Fines and Their Application in the Synthesis of Hybrid Hydrogels
In this work, hybrid hydrogels were synthesized with the inclusion of two types of clay materials that are considered industrial waste: red mud (RM) and ferrosilicomanganese fines (FeSiMn). These solid waste materials were characterized by studying their particle size and chemical composition, which...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2022 |
| País: | España |
| Institución: | Universidad del País Vasco |
| Repositorio: | Addi. Archivo Digital para la Docencia y la Investigación |
| OAI Identifier: | oai:addi.ehu.eus:10810/58250 |
| Acceso en línea: | http://hdl.handle.net/10810/58250 |
| Access Level: | acceso abierto |
| Palabra clave: | red mud modification hybrid hydrogel |
| Sumario: | In this work, hybrid hydrogels were synthesized with the inclusion of two types of clay materials that are considered industrial waste: red mud (RM) and ferrosilicomanganese fines (FeSiMn). These solid waste materials were characterized by studying their particle size and chemical composition, which are two key variables for their application in the synthesis of hybrid hydrogels. The morphology imaged by transmission electron microscopy (TEM) and scanning electron microscopy (SEM), showed, in the case of RM, heterogeneous size and shape particles, with 73% of the particles having lengths of less than 5 μm. On the other hand, FeSiMn had particles with a circular morphology of nanometric sizes. Regarding the synthesis of the hybrid hydrogels, it was determined that the incorporation of small percentages (0.1%) of the inorganic phases improved the capacity of the materials to absorb water (swelling indices of 1678% and 1597% for the RM and FeSiMn hydrogels, respectively) compared to the conventional polyacrylamide hydrogel (1119%). An improvement in Vickers microhardness and storage modulus (G′) was also observed: the hybrid with 10% RM presented a G′, 50 times higher than conventional hydrogel. The results show the merit of RM and FeSiMn in improving the properties of hydrogels. |
|---|