Structural changes during the natural aging process of InN quantum dots
The natural aging process of InN nanostructures by the formation of indium oxides is examined by transmission electron microscopy related techniques. Uncapped and GaN-capped InN quantum dots (QDs) on GaN/sapphire substrates were grown under the same conditions and kept at room temperature/pressure c...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2009 |
| País: | España |
| Institución: | Universidad de Sevilla (US) |
| Repositorio: | idUS. Depósito de Investigación de la Universidad de Sevilla |
| OAI Identifier: | oai:idus.us.es:11441/126828 |
| Acceso en línea: | https://hdl.handle.net/11441/126828 https://doi.org/10.1063/1.3010309 |
| Access Level: | acceso abierto |
| Palabra clave: | Atoms Gallium alloys Gallium nitride Indium Nanostructures |
| Sumario: | The natural aging process of InN nanostructures by the formation of indium oxides is examined by transmission electron microscopy related techniques. Uncapped and GaN-capped InN quantum dots (QDs) on GaN/sapphire substrates were grown under the same conditions and kept at room temperature/pressure conditions. The GaN capping layer is found to preserve the InN QDs in the wurtzite phase, avoiding the formation of group-III oxides, while in the uncapped sample, a thin layer of cubic phases are formed that envelops the nucleus of wurtzite InN. These cubic phases are shown to be mainly bcc- In 2 O3 for long aged samples where the nitrogen atoms in the InN surface layers have been substituted by atmospheric oxygen. This process implies the gradual transformation of the In sublattice from hcp to a quasi-fcc structure. Metastable zinc-blende InN phases rich in oxygen atoms are proposed to act as intermediate phases and they are evinced in samples less aged. The large concurrence of interplanar spaces, the twin formation, and the existence of a free surface that facilitates the transformation support this mechanism and would explain the high instability of the InN nanostructures at ambient conditions. |
|---|