Aluminum Guefoams Coated with Reduced Graphene Oxide: A Corrosion Protection Study.
[EN] To enhance their corrosion protection, Guefoams were coated with RGO using both potentiostatic and potentiodynamic methods. The potentiodynamic method produced the thickest RGO coating and the lowest Cl, O, and Al content, as observed using FESEM and EDX. The Guefoams were exposed to a 3.5% NaC...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2024 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/209094 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/209094 |
| Access Level: | acceso abierto |
| Palabra clave: | Reduced graphene oxide Guefoam Aluminum Corrosion protection QUIMICA FISICA 03.- Garantizar una vida saludable y promover el bienestar para todos y todas en todas las edades |
| Sumario: | [EN] To enhance their corrosion protection, Guefoams were coated with RGO using both potentiostatic and potentiodynamic methods. The potentiodynamic method produced the thickest RGO coating and the lowest Cl, O, and Al content, as observed using FESEM and EDX. The Guefoams were exposed to a 3.5% NaCl solution and steam. The polarization resistance was examined, electrochemical impedance spectroscopy was performed, and polarization curves were constructed to monitor the corrosion process. After 28 days, the Al concentrations in the solutions were measured, and were found to be 145 mg/L (bare Guefoam), 70 mg/L (RGO-coated, potentiostatic), and 35 mg/L (RGO-coated, potentiodynamic). The potentiodynamic RGO coating also showed the best corrosion protection values. |
|---|