Mechanical Properties of Low-Temperature Bainite
The mechanical properties of a bainitic microstructure with slender ferrite plates (20-65 nm in thickness) in a matrix of carbon-enriched retained austenite were characterized. The microstructure is generated by isothermal transformation at temperatures in the range 200-300ºC. A yield strength as hi...
| Autores: | , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2005 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/83004 |
| Acceso en línea: | http://hdl.handle.net/10261/83004 |
| Access Level: | acceso abierto |
| Palabra clave: | Low temperature bainite Mechanical properties Dislocation density Carbon content |
| Sumario: | The mechanical properties of a bainitic microstructure with slender ferrite plates (20-65 nm in thickness) in a matrix of carbon-enriched retained austenite were characterized. The microstructure is generated by isothermal transformation at temperatures in the range 200-300ºC. A yield strength as high as 1.5 GPa and an ultimate tensile strength between 1.77 to 2.2 GPa was achieved, depending on the transformation temperature. Furthermore, the high strength is frequently accompanied by ductility (£ 30%) and respectable levels of fracture toughness (< 45 MPa m0.5). This unusual combination of properties is attributed to the exceptionally fine scale of the carbidefree bainitic microstructure and the associated retained austenite. |
|---|