Reverse water-gas shift reaction at the Cu/ZnO interface: Influence of the Cu/Zn ratio on structure-activity correlations
[ENn] The physicochemical properties of hydroxycarbonate-based precipitates [zincian malachite (ZM) and aurichalcite precursors], calcined CuO/ZnO precatalysts and finally reduced Cu/ZnO catalysts, with several Cu-Zn ratios, have been investigated by different characterization techniques. Results fr...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2016 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:dnet:digitalcsic_::2ace39163acd78157a34596a959de1ca |
| Acceso en línea: | http://hdl.handle.net/10261/202741 |
| Access Level: | acceso abierto |
| Palabra clave: | Cu/ZnO catalyst zincian malachite and aurichalcite precursors rWGS reaction Cu-Zn interface |
| Sumario: | [ENn] The physicochemical properties of hydroxycarbonate-based precipitates [zincian malachite (ZM) and aurichalcite precursors], calcined CuO/ZnO precatalysts and finally reduced Cu/ZnO catalysts, with several Cu-Zn ratios, have been investigated by different characterization techniques. Results from isothermal physisorption of N (BET), X-ray Diffraction (XRD), Temperature Programmed Reduction (TPR), NO Reactive Frontal Chromatography (NO-RFC), X-ray Photoelectron Spectroscopy (XPS) and Scanning Electron Microscopy (SEM) have been correlated with the catalytic activity for the reverse water-gas shift (rWGS) reaction in order to provide insight into the controversial nature of active species in carbon dioxide activation, respectively the role of Cu and ZnO. Average crystalline domain size of CuO and ZnO show a relationship with the amount of each phase in the calcined sample. This is in agreement with the TPR profiles, which indicate a better dispersion of Cu for the ZnO-rich samples and a shift for the first reduction step to higher temperatures (T for Cu to Cu). XPS measurements point out the surface enrichment of ZnO is less pronounced with higher ZnO/(ZnO + Cu) ratios. Activity results show that catalysts derived from high surface area ex-aurichalcite (Zn content, 50-70% atom) catalysts are more active in rWGS with lower apparent activation energies than ex-ZM catalysts (Zn content, 15-30% atom) with comparable apparent Cu surface area/NO capacity. Thus, the CO formation rate as function of the apparent Cu surface area indicates that the reaction rate is not dependent on the exposed apparent Cu surface, but from an adjusted interface composition predetermined by the precursor structure and its thermal post-treatment. |
|---|