Sustainable β- and γ-cyclodextrins for development of highly permeable thin film composite nanofiltration membranes
The use of macromolecules, such as cyclodextrins (CDs), given their porosity and compatibility with organic materials, are very attractive for the progress of polymeric membranes in nanofiltration (NF) of aqueous dye solutions. Two types of membranes were fabricated. Firstly, β- and γ-CDs were incor...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2023 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/344542 |
| Acceso en línea: | http://hdl.handle.net/10261/344542 |
| Access Level: | acceso abierto |
| Palabra clave: | Membrane Nanofiltration Thin film composite Polyamide Polyester Cyclodextrins |
| Sumario: | The use of macromolecules, such as cyclodextrins (CDs), given their porosity and compatibility with organic materials, are very attractive for the progress of polymeric membranes in nanofiltration (NF) of aqueous dye solutions. Two types of membranes were fabricated. Firstly, β- and γ-CDs were incorporated to polyamide (PA) thin film composite (TFC) membranes. These membranes, named CD/MPD-TMC, were prepared by conventional interfacial polymerization —i.e., an aqueous solution of m-phenylenediamine (MPD) followed by a solution of trimesoyl chloride (TMC) in hexane— by replacing a certain amount of the MPD monomer with varying proportions of CDs. Secondly, two-step double-IP (TD-IP) membranes were fabricated as follows: CDs were deposited atop the polymer support, followed by addition of TMC —forming a polyester (PE) layer—, and subsequently the membrane surface was modified with MPD molecules. In both CD/MPD-TMC and TD-IP membranes, the presence of CDs improved the membrane performance, the latter configuration leading to much higher water permeances. The TD-IP membrane using β-CD achieved the highest water permeance of 10 L m−2 h−1·bar−1 (LMH bar−1) and a rejection of acridine orange dye (265 Da) greater than 98 %. This represents a 6-fold increase in water permeance compared to bare PA (1.6 LMH bar−1). The enhanced water transport was mainly attributed to the more hydrophilic nature of the membranes and the presence of a PE layer with a porous structure and high pore connectivity. High dye rejection resulted from electrostatic and Donnan repulsions due to surface modification with MPD molecules. |
|---|