Development of Co-Rich Microwires with Graded Magnetic Anisotropy
In this paper, a gradual change in the hysteresis loop of Co-rich glass-coated microwire stress-annealed at variable temperature is observed. Such microwires annealed with a temperature gradient also present a variable squareness ratio and magnetic anisotropy field along the microwire’s length. The...
| Autores: | , , , , , |
|---|---|
| Formato: | artículo |
| Fecha de publicación: | 2021 |
| País: | España |
| Recursos: | Universidad del País Vasco |
| Repositorio: | Addi. Archivo Digital para la Docencia y la Investigación |
| OAI Identifier: | oai:addi.ehu.eus:10810/54993 |
| Acesso em linha: | http://hdl.handle.net/10810/54993 |
| Access Level: | acceso abierto |
| Palavra-chave: | magnetic microwires magnetic anisotropy thermal treatment |
| Resumo: | In this paper, a gradual change in the hysteresis loop of Co-rich glass-coated microwire stress-annealed at variable temperature is observed. Such microwires annealed with a temperature gradient also present a variable squareness ratio and magnetic anisotropy field along the microwire’s length. The obtained graded anisotropy has been attributed to a gradual modification of the domain structure along the microwire originated by a counterbalance between shape, magnetoelastic, and induced magnetic anisotropies. Accordingly, we propose a rather simple route to design graded magnetic anisotropy in a magnetic microwire. |
|---|