Nanocrystalline M-type hexaferrite powders: preparation, geometric and magnetic propertiess
Co-Ti-Sn-Ge substituted M-type bariumhexaferrite powders with mean grain sizes between about 10 nm and about 1 ¿m and a narrow size distribution were prepared reproducibly by means of a modified glass crystallization method. At annealing temperatures between 560 and 580°C of the amorphous flakes nan...
| Autores: | , , , , , , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 1994 |
| País: | España |
| Recursos: | Universidad de Barcelona |
| Repositorio: | Dipòsit Digital de la UB |
| OAI Identifier: | oai:diposit.ub.edu:2445/8582 |
| Acesso em linha: | https://hdl.handle.net/2445/8582 |
| Access Level: | acceso abierto |
| Palavra-chave: | Materials nanoestructurats Propietats magnètiques Materials magnètics Anisotropia Substàncies amorfes Nanostructured materials Magnetic properties Magnetic materials Anisotropy Amorphous substances |
| Resumo: | Co-Ti-Sn-Ge substituted M-type bariumhexaferrite powders with mean grain sizes between about 10 nm and about 1 ¿m and a narrow size distribution were prepared reproducibly by means of a modified glass crystallization method. At annealing temperatures between 560 and 580°C of the amorphous flakes nanocrystalline particles grow. They behave superparamagnetically at room temperature and change into stable magnetic single domains at lower temperatures. The magnetic volume of the powders is considerably less than the geometric one. However, the effective anisotropy fields are larger by a Factor of two to three. |
|---|