Active Er3+ doped lead-niobium-germanate planar waveguides produced by pulsed laser deposition
In this work, pulsed laser deposition has been used to produce Er3+ doped lead-niobium-germanate thin films from Er3+ doped 50Geo2-25PbO-25Nb2O5 transparent glasses with an Er2O3 content in the 0.5-3 weight % range. In all cases, by pumping the 4I11/2 level of Er3+, the as deposited films are optica...
| Autores: | , , , , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2003 |
| País: | España |
| Recursos: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/224112 |
| Acesso em linha: | http://hdl.handle.net/10261/224112 |
| Access Level: | acceso abierto |
| Palavra-chave: | Heavy metal oxide glasses Thin films Erbium Pulsed laser deposition |
| Resumo: | In this work, pulsed laser deposition has been used to produce Er3+ doped lead-niobium-germanate thin films from Er3+ doped 50Geo2-25PbO-25Nb2O5 transparent glasses with an Er2O3 content in the 0.5-3 weight % range. In all cases, by pumping the 4I11/2 level of Er3+, the as deposited films are optically active showing at room temperature the 4I13/2 →4I15/2 emission centered around 1530 nm. The luminescence intensity increases as the Er3+ content in the targets increases, whereas the opposite behavior is observed for the luminescence lifetime. The emission intensity and lifetimes of the 1.5 μm emission increase upon annealing. |
|---|