Luminescence from growth topographic features in GaN : Si films
Cathodoluminescence (CL) in the scanning electron microscope is used to investigate the nature of defects responsible for the luminescence associated with round and hexagonal-like topographic features of GaN:Si films. Round hillocks of the size of a few microns, which sometimes have a nanopipe relat...
| Autores: | , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 1998 |
| País: | España |
| Institución: | Universidad Complutense de Madrid (UCM) |
| Repositorio: | Docta Complutense |
| Idioma: | inglés |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/59162 |
| Acceso en línea: | https://hdl.handle.net/20.500.14352/59162 |
| Access Level: | acceso abierto |
| Palabra clave: | 538.9 Física de materiales |
| Sumario: | Cathodoluminescence (CL) in the scanning electron microscope is used to investigate the nature of defects responsible for the luminescence associated with round and hexagonal-like topographic features of GaN:Si films. Round hillocks of the size of a few microns, which sometimes have a nanopipe related central hole, do not influence the luminescence emission of the film. Hillocks with sizes of several tens of microns show a marked CL contrast at the center and at the border. The origin of the observed contrast is attributed to a growth induced inhomogeneous distribution of point defects and impurities. Radiation with the electron beam of the scanning microscope causes a decrease of the CL intensity without spectral changes. |
|---|