Defect study of SnO2 nanostructures by cathodoluminescence analysis: Application to nanowires
Defects in SnO2 nanowires have been studied by cathodoluminescence, and the obtained spectra have been compared with those measured on SnO2 nanocrystals of different sizes in order to reveal information about point defects not determined by other characterization techniques. Dependence of the lumine...
| Autores: | , , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2006 |
| País: | España |
| Institución: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositorio: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:2445/7581 |
| Acceso en línea: | https://hdl.handle.net/2445/7581 |
| Access Level: | acceso abierto |
| Palabra clave: | Detectors Nanotecnologia SnO2 Cathodoluminescence Nanostructures Nanowire Oxygen vacancy |
| Sumario: | Defects in SnO2 nanowires have been studied by cathodoluminescence, and the obtained spectra have been compared with those measured on SnO2 nanocrystals of different sizes in order to reveal information about point defects not determined by other characterization techniques. Dependence of the luminescence bands on the thermal treatment temperatures and pre-treatment conditions have been determined pointing out their possible relation, due to the used treatment conditions, with the oxygen vacancy concentration. To explain these cathodoluminescence spectra and their behavior, a model based on first-principles calculations of the surface oxygen vacancies in the different crystallographic directions is proposed for corroborating the existence of surface state bands localized at energy values compatible with the found cathodoluminescence bands and with the gas sensing mechanisms. CL bands centered at 1.90 and 2.20 eV are attributed to the surface oxygen vacancies 100° coordinated with tin atoms, whereas CL bands centered at 2.37 and 2.75 eV are related to the surface oxygen vacancies 130° coordinated. This combined process of cathodoluminescence and ab initio calculations is shown to be a powerful tool for nanowire defect analysis. |
|---|