Development of a Fluorine-Free Polymer-Assisted-Deposition Route for YBa2Cu3O7−x Superconducting Films
Polymer assisted deposition (PAD) was used as an environmentally friendly, non-fluorine, growth method for superconducting YBa2Cu3O7−x (YBCO) films. The kinetics of the thermal decomposition of the precursor powder was studied by thermogravimetry coupled with mass spectrometry (TG-QMS). YBCO films w...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2020 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/233192 |
| Acceso en línea: | http://hdl.handle.net/10261/233192 |
| Access Level: | acceso abierto |
| Palabra clave: | Fluorine-free coating solution Polymer assisted deposition YBCO superconducting films |
| Sumario: | Polymer assisted deposition (PAD) was used as an environmentally friendly, non-fluorine, growth method for superconducting YBa2Cu3O7−x (YBCO) films. The kinetics of the thermal decomposition of the precursor powder was studied by thermogravimetry coupled with mass spectrometry (TG-QMS). YBCO films were spin coated on (100) SrTiO3 (STO) single crystalline substrates, followed by a single step thermal treatment under wet and dry O2 and O2/N2 mixture. The as-obtained films were epitaxially grown having a [001]YBCO||[001]STO out-of-plane epitaxial relationship and exhibited good superconducting properties with Tc (R = 0) > 88 K, transition widths, ΔT ≈ 2 K and critical current densities as high as 2.3 MA/cm2 at 77 K and self magnetic field. |
|---|