The role of carbon nanotubes on the stability of tetragonal zirconia polycrystals
The effect of single walled carbon nanotubes (SWNT) at zirconia grain boundaries on the stability of a tetragonal zirconia polycrystalline matrix has been explored in as–sintered composites and after low–temperature hydrothermal degradation (LTD) experiments. For this purpose, highly–dense 3 mol% YO...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2018 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/193208 |
| Acceso en línea: | http://hdl.handle.net/10261/193208 |
| Access Level: | acceso abierto |
| Palabra clave: | Carbon nanotubes ZrO2 Phase transformation LTD |
| Sumario: | The effect of single walled carbon nanotubes (SWNT) at zirconia grain boundaries on the stability of a tetragonal zirconia polycrystalline matrix has been explored in as–sintered composites and after low–temperature hydrothermal degradation (LTD) experiments. For this purpose, highly–dense 3 mol% YO–doped tetragonal zirconia polycrystalline (3YTZP) ceramics and SWNT/3YTZP composites were prepared by spark plasma sintering (SPS). Quantitative X–ray diffraction analysis and microstructural observations point out that an increasing amount of well–dispersed SWNT bundles surrounding zirconia grains decreases the metastable tetragonal phase retention in the ceramic matrix after sintering. In contrast, the tetragonal ceramic grains in composites with SWNTs are less sensitive to the presence of water, i.e. to undergo a martensitic transformation under LTD conditions, than monolithic 3YTZP ceramics. The SWNT incorporation diminishes micro–cracking due to tetragonal to monoclinic ZrO phase transformation in the composites. |
|---|