Friction capabilities of graphite-based lubricants at room and over 1400 K temperatures
The present work investigates the lubricant capabilities at room and hot-forging temperatures (>1400 K) of three types of lubricants with two different graphite concentrations (8% and 12%). These lubricants are distinguished by measuring the percentage of chemical elements and average size of gra...
| Autor: | |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2019 |
| País: | España |
| Institución: | Universitat Politècnica de Catalunya (UPC) |
| Repositorio: | UPCommons. Portal del coneixement obert de la UPC |
| Idioma: | inglés |
| OAI Identifier: | oai:upcommons.upc.edu:2117/133086 |
| Acceso en línea: | https://hdl.handle.net/2117/133086 https://dx.doi.org/10.1007/s00170-019-03290-4 |
| Access Level: | acceso abierto |
| Palabra clave: | Friction Graphitic lubricant . Extreme temperatures . Friction coefficients . Ring test . Hot-forging Fricció Àrees temàtiques de la UPC::Enginyeria mecànica |
| Sumario: | The present work investigates the lubricant capabilities at room and hot-forging temperatures (>1400 K) of three types of lubricants with two different graphite concentrations (8% and 12%). These lubricants are distinguished by measuring the percentage of chemical elements and average size of graphite particles. Later, two standardized methods, i.e., pin-on disc and ring test, are utilized to assess the main friction differences under laboratory and real industry conditions, respectively. The results exhibit that the friction values at room temperature are lower for lubricant B, no matter which type of graphite concentration is used, whereas at hot-forging temperatures, greater percentage of graphite enhances lower frictional values when higher deformations are assessed. Additionally, the ring tests performed at hot-forging temperatures show significant tribology differences when the degree of deformation reaches 50%. Particularly, the lubricant B shows the lowest values of friction coefficients of 0.22 and 0.21 for 8% and 12%of graphite concentration, respectively. Therefore, it can be concluded that the selection of a proper type of lubricant (regarding chemical composition and size of solid suspension) and the graphite concentration are sensitive parameters, when it comes to achieve different bulk deformations combined with extreme temperatures like in hot-forging process |
|---|