Nanocomposites of Multiphase Polymer Blend Reinforced with Carbon Nanotubes: Processing and Characterization
This thesis presents the study of nanocomposites based on immiscible polymer blend of polycarbonate and acrylonitrile-butadiene-styrene (PC/ABS) filled with multi-walled carbon nanotubes (MWCNT). The aim is to achieve an improvement of mechanical properties and electrical conductivity of the nanocom...
| Autor: | |
|---|---|
| Tipo de recurso: | tesis doctoral |
| Fecha de publicación: | 2014 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/36869 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/36869 |
| Access Level: | acceso abierto |
| Palabra clave: | Nanocomposite Carbon nanotube Multi-phase polymer blend Compounding Injection molding. CIENCIA DE LOS MATERIALES E INGENIERIA METALURGICA |
| Sumario: | This thesis presents the study of nanocomposites based on immiscible polymer blend of polycarbonate and acrylonitrile-butadiene-styrene (PC/ABS) filled with multi-walled carbon nanotubes (MWCNT). The aim is to achieve an improvement of mechanical properties and electrical conductivity of the nanocomposites. In an initial stage, a twin-screw extruder was used to obtain nanocomposites by melt compounding. Three methods of carbon nanotubes addition were studied: direct addition, dilution from a masterbatch and feeding of MWCNT suspension in ethanol. For each method, the influence of nanofiller content and processing parameters on morphology and final properties of the nanocomposite was analyzed. Furthermore, the influence of two types of carbon nanotubes modifications was studied: covalent modification by surface-oxidation (MWCNT-COOH) and non-covalent modification by an addition of surfactant promoting the nanofiller-matrix interactions. A good dispersion of the MWCNT was obtained for masterbatch dilution and suspension feeding. Both methods showed preferential localization of carbon nanotubes in polycarbonate phase (PC). Samples processed by masterbatch dilution showed the 30 % increase of rigidity and a decrease of ductility of PC/ABS for 0.5 wt. % MWCNT. Electrical conductivity was influenced by processing temperature and carbon nanotubes type. The percolation threshold value was 2.0 wt. % for pristine MWCNT and 1.5 wt. % for modified MWCNT-COOH. Better balance of mechanical properties and electrical conductivity was achieved in the samples obtained by the masterbatch route. These properties were studied in a subsequent phase, when the extruded nanocomposite was injection molded in order to obtain a defined geometry. |
|---|