Synthesis and characterization of FePt/Au core-shell nanoparticles
In this work, the structural and magnetic properties of the gold- coated FePt nanoparticles synthesized from high- temperature solution phase are presented. The amount of gold was optimized to obtain most of the FePt particles coated. The particle diameter increases from 4 to 10 nm as observed by TE...
| Autores: | , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2007 |
| País: | España |
| Institución: | Universidad Complutense de Madrid (UCM) |
| Repositorio: | Docta Complutense |
| Idioma: | inglés |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/52149 |
| Acceso en línea: | https://hdl.handle.net/20.500.14352/52149 |
| Access Level: | acceso abierto |
| Palabra clave: | 538.9 Magnetic-properties Fe Física de materiales Física del estado sólido 2211 Física del Estado Sólido |
| Sumario: | In this work, the structural and magnetic properties of the gold- coated FePt nanoparticles synthesized from high- temperature solution phase are presented. The amount of gold was optimized to obtain most of the FePt particles coated. The particle diameter increases from 4 to 10 nm as observed by TEM. The magnetic properties are largely affected by the coating. At low temperature, the coercive. field Hc of the coated nanoparticles decreases about three times respect to the uncoated and the blocking temperature reduces to the half. The changes of the magnetic behavior are discussed in terms of the effect of the gold atoms at the FePt core surface. |
|---|