Photocatalytic hydrogen evolution using bi-metallic (Ni/Pt) Na2Ti3O7 whiskers: Effect of the deposition order
Photocatalytic hydrogen production through ethanol photo-reforming using Na2Ti3O7 whiskers increases if the sodium titanate is decorated with well-known metallic catalysts such as Ni and Pt. Whereas wet impregnation with nickel gives only a slight increase in the activity, photo-deposition of Pt inc...
| Autores: | , , , , , |
|---|---|
| Tipo de documento: | artigo |
| Estado: | Versão publicada |
| Data de publicação: | 2019 |
| País: | España |
| Recursos: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositório: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:2445/176315 |
| Acesso em linha: | https://hdl.handle.net/2445/176315 |
| Access Level: | Acceso aberto |
| Palavra-chave: | Fotocatàlisi Alcohol Catalitzadors metàl·lics Photocatalysis Metal catalysts |
| Resumo: | Photocatalytic hydrogen production through ethanol photo-reforming using Na2Ti3O7 whiskers increases if the sodium titanate is decorated with well-known metallic catalysts such as Ni and Pt. Whereas wet impregnation with nickel gives only a slight increase in the activity, photo-deposition of Pt increased the H2 production by more than one order of magnitude. Through the combination of both co-catalysts (Ni and Pt) a superior performance in terms of H2 production is further observed. However, hydrogen yield is largely enhanced (almost three-fold), up to 778 μmol·g−1·h−1, if the Pt is photo-deposited on the surface of the catalyst before wet impregnation with Ni species (NTO/Pt/Ni) compared to H2 yield (283 μmol·g−1·h−1) achieved with the catalyst prepared in the reverse order (NTO/Ni/Pt). Structural, morphological, optical, and chemical characterization was carried out in order to correlate physicochemical properties with their photocatalytic activity. The X-ray photoelectron spectroscopy (XPS) results show a higher concentration of Pt2+ species if this metallic layer is under the nickel oxide layer. Moreover, X-ray diffraction patterns (XRD) show that Na2Ti3O7 surface is modified for both metal decoration processes. |
|---|