[EN] The one-pass conversion of renewable syngas into aromatics, particularly to BTX (benzene, toluene, xylenes) and para-xylene (PX), represents a promising approach to produce high-value sustainable chemicals from non-fossil resources. In this work, a systematic study of the modification of HZSM-5...
| Autores: | , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2025 |
| País: | España |
| Institución: | Universidad de Barcelona (UB) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/220939 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/220939 |
| Access Level: | acceso abierto |
| Palabra clave: | Syngas Aromatics BTX,para-xylene Oxide-zeolite catalyst Zn-ZrO2 ZSM-5 Large crystal size |
| Sumario: | [EN] The one-pass conversion of renewable syngas into aromatics, particularly to BTX (benzene, toluene, xylenes) and para-xylene (PX), represents a promising approach to produce high-value sustainable chemicals from non-fossil resources. In this work, a systematic study of the modification of HZSM-5 zeolite by surface silylation and incorporation of MgO was performed aiming at maximising the BTX and PX selectivity in the syngas-to-aromatics (STA) reaction using tandem Zn-ZrO2+HZSM-5 catalysts following the methanol route. A zeolite with unusually large crystal size was purposedly used to intensify the shape selectivity effect. This zeolite exhibited high BTX selectivity (53.0 % in aromatics) albeit poor stability with TOS. Generation of a proper amount of mesopores via controlled desilication improved the catalyst stability and the aromatics selectivity (from 59.2 % up to 73.2 %) at the cost of lowering the BTX selectivity. Effective passivation of the external Br & Oslash;nsted acid sites was reached by submitting the mesoporous zeolite to four silylation cycles with TEOS. The silylation treatment significantly raised the BTX selectivity to 52.1 % while maintaining high selectivity of total aromatics (67.9 %), but had only a moderate positive effect on PX selectivity. Incorporation of Mg species in the silylated zeolite produced the largest impact on PX selectivity, attaining an outstanding value of 76.8 % in xylenes (41.2 % in aromatics) upon loading 3 wt% Mg. |
|---|