Microcellular foamed aromatic polyamides (aramids). Structure, thermal and mechanical properties
We have deeply diminished the density of high performance aromatic polyamides or aramids. Thus, we have prepared microcellular films that at the same time maintain the outstanding thermal and mechanical properties characteristic of these high performance materials. Two different cellular aramids wer...
| Autores: | , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión aceptada para publicación |
| Fecha de publicación: | 2018 |
| País: | España |
| Institución: | Universidad de Burgos (UBU) |
| Repositorio: | Repositorio Institucional de la Universidad de Burgos (RIUBU) |
| OAI Identifier: | oai:riubu.ubu.es:10259/5025 |
| Acceso en línea: | http://hdl.handle.net/10259/5025 |
| Access Level: | acceso abierto |
| Palabra clave: | Aramids Microcellular Ionic liquids ScCO2 foaming Polyamide Química orgánica Ingeniería química Chemistry, Organic Chemical engineering |
| Sumario: | We have deeply diminished the density of high performance aromatic polyamides or aramids. Thus, we have prepared microcellular films that at the same time maintain the outstanding thermal and mechanical properties characteristic of these high performance materials. Two different cellular aramids were produced, based on commercial poly(m-phenylene isophthalamide), one of them with an additional azide group. Microcellular structures have been obtained by adding ionic liquids combined to ScCO2 foaming process, with cell sizes between 0.6 and 4.7 µm and cell densities between 109 and 1011 cells cm3. The density was lowered for the commercial poly(m-phenylene isophthalamide) (Nomex® and Teijin Conex®) from 1.43 to 0.62 g cm−3 and from 1.48 to 0.31 g cm3 for the aramid containing the azide group. Foams present the following thermal and mechanical properties: 5% weight loss observed at T > 400 °C and relative Young modulus and tensile strength of 1.2 GPa (g cm−3)−1 and 60 MPa (g cm−3)−1, respectively. |
|---|