Poly(methyl methacrylate) as Healing Agent for Carbon Fibre Reinforced Epoxy Composites
Self-healing materials offer a potential solution to the problem of damage to fibre-reinforced plastics (FRPs) by allowing for the in-service repair of composite materials at a lower cost, in less time, and with improved mechanical properties compared to traditional repair methods. This study invest...
| Autores: | , , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2023 |
| País: | España |
| Recursos: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/329586 |
| Acesso em linha: | http://hdl.handle.net/10261/329586 |
| Access Level: | acceso abierto |
| Palavra-chave: | thermoplastic Coating self-healing carbon fibre fracture toughness |
| Resumo: | Self-healing materials offer a potential solution to the problem of damage to fibre-reinforced plastics (FRPs) by allowing for the in-service repair of composite materials at a lower cost, in less time, and with improved mechanical properties compared to traditional repair methods. This study investigates for the first time the use of poly(methyl methacrylate) (PMMA) as a self-healing agent in FRPs and evaluates its effectiveness both when blended with the matrix and when applied as a coating to carbon fibres. The self-healing properties of the material are evaluated using double cantilever beam (DCB) tests for up to three healing cycles. The blending strategy does not impart a healing capacity to the FRP due to its discrete and confined morphology; meanwhile, coating the fibres with the PMMA results in healing efficiencies of up to 53% in terms of fracture toughness recovery. This efficiency remains constant, with a slight decrease over three subsequent healing cycles. It has been demonstrated that spray coating is a simple and scalable method of incorporating a thermoplastic agent into an FRP. This study also compares the healing efficiency of specimens with and without a transesterification catalyst and finds that the catalyst does not increase the healing efficiency, but it does improve the interlaminar properties of the material. |
|---|