Recrystallisation Driving and Pinning Forces during Hot Rolling of a Low Nb-Microalloyed Steel
The values of recrystallisation driving (FR) and pinning forces (FP) during the hot rolling of a low Nb-microalloyed steel were calculated using several expressions found in the literature. A comparative study of the hypothesis into the interaction between precipitates and migrating grain boundaries...
| Autores: | , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2005 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/56330 |
| Acceso en línea: | http://hdl.handle.net/10261/56330 |
| Access Level: | acceso abierto |
| Palabra clave: | Driving force Hot rolling Micro-Alloyed steel Pinning force Static recrystallization |
| Sumario: | The values of recrystallisation driving (FR) and pinning forces (FP) during the hot rolling of a low Nb-microalloyed steel were calculated using several expressions found in the literature. A comparative study of the hypothesis into the interaction between precipitates and migrating grain boundaries was carried out, and the methods for estimating volume fractions of precipitates and dislocation density were assessed. Though the criterion selected greatly influences the values obtained for both forces, FP grows faster than FR as the rolling temperature drops. |
|---|