Large enhancement of thermal conductance at ambient and cryogenic temperatures by laser remelting of plasma-sprayed Al2O3 coatings on Cu
Joints of high thermal contact conductance and electrical insulation have been obtained by coating copper supports with thin alumina (Al2O3) layers (of 140–150 μm thickness). This has been achieved by a combination of plasma spraying process and the subsequent coating remelting by a near-Infrared (n...
| Autores: | , , , , , |
|---|---|
| Formato: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2021 |
| País: | España |
| Recursos: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositorio: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:2445/219017 |
| Acesso em linha: | https://hdl.handle.net/2445/219017 |
| Access Level: | acceso abierto |
| Palavra-chave: | Superconductivitat a altes temperatures Revestiments High temperature superconductivity Coatings |
| Resumo: | Joints of high thermal contact conductance and electrical insulation have been obtained by coating copper supports with thin alumina (Al2O3) layers (of 140–150 μm thickness). This has been achieved by a combination of plasma spraying process and the subsequent coating remelting by a near-Infrared (n-IR) laser. With a proper optimization of the laser processing conditions, it is possible to transform the metastable γ-Al2O3 phase of the assprayed coatings to stable α-Al2O3, and to achieve denser alumina coatings. This results in a large enhancement of the thermal conductance of the joints, enabling their application as heat sinks at cryogenic and ambient temperatures. The process proposed in this work is scalable for the formation of alumina coatings on large metallic pieces of complex geometries. |
|---|