Micropillar compression of Ti(C,N)-FeNi cermets: Microstructural, processing, and scale effects
[EN] The influence of microstructure and processing route on the small-scale mechanical response as well as on the deformation and failure mechanisms of Ti(C,N)-FeNi cermets were investigated by uniaxial compression of micropillars milled by focused ion beam with different sizes. Stress-strain curve...
| Autores: | , , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2023 |
| País: | España |
| Institución: | Consejo Superior de Investigaciones Científicas (CSIC) |
| Repositorio: | DIGITAL.CSIC. Repositorio Institucional del CSIC |
| OAI Identifier: | oai:digital.csic.es:10261/349763 |
| Acceso en línea: | http://hdl.handle.net/10261/349763 |
| Access Level: | acceso abierto |
| Palabra clave: | Micropillar Uniaxial compression Cermet Powder metallurgy Deformation mechanisms |
| Sumario: | [EN] The influence of microstructure and processing route on the small-scale mechanical response as well as on the deformation and failure mechanisms of Ti(C,N)-FeNi cermets were investigated by uniaxial compression of micropillars milled by focused ion beam with different sizes. Stress-strain curves were determined and associated deformation mechanisms were observed in-situ using scanning electron microscopy. The appropriate micropillars dimension was assessed, based on the microstructural characteristics of studied cermets, to overcome scale effect issues. A direct relationship was observed between yield strength and ceramic/metal ratio for colloidal samples. Meanwhile, deformation of metallic binder and glide between Ti(C,N)/Ti(C,N) particles were evidenced as dominant mechanisms during the compression for colloidal cermets with 70 and 80 vol% of ceramic phase, respectively. The obtained results illustrate that samples processed from powder attained by colloidal route provide superior mechanical behavior, as compared to that exhibited by specimens shaped following a conventional powder metallurgy one (wet ball-milling/drying). |
|---|