A data reduction method based on the J-integral to obtain the interlaminar fracture toughness in a mode II end-loaded split (ELS) test
Various difficulties arise in the data reduction of the end-loaded split (ELS) test. On one hand, a small Fracture Process Zone (FPZ) at the crack front is assumed in the existing mode II end-loaded split test methodologies based on Linear Elastic Fracture Mechanics (LEFM). However, mode II fracture...
| Autores: | , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2016 |
| País: | España |
| Institución: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositorio: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:10256/12720 |
| Acceso en línea: | http://hdl.handle.net/10256/12720 |
| Access Level: | acceso embargado |
| Palabra clave: | Assaigs de materials Materials -- Testing Materials compostos -- Deslaminatge Composite materials -- Delamination Mecànica de fractura Fracture mechanics |
| Sumario: | Various difficulties arise in the data reduction of the end-loaded split (ELS) test. On one hand, a small Fracture Process Zone (FPZ) at the crack front is assumed in the existing mode II end-loaded split test methodologies based on Linear Elastic Fracture Mechanics (LEFM). However, mode II fracture has been reported to involve large FPZ and a fuzzy crack tip. Furthermore, the ELS test, is usually affected by geometrical non-linearities. This work proposes a closed-form solution based on the J-integral to determine the interlaminar fracture toughness in an ELS test. This solution avoids the need to measure the crack length, and is applicable when a large FPZ is present, as occurs in adhesive bonded joints between CFRP. In addition, because the ELS test involves large vertical deflections, a correction of the formulation for large displacements has been implemented. This new methodology has been compared to other methods available in the literature based on LEFM by means of an experimental campaign of delamination tests using unidirectional CFRP specimens in order to make a first validation of the method |
|---|