MAPbI2.9-xBrxCl0.1 hybrid halide perovskites: Shedding light on the effect of chloride and bromide ions on structural and photoluminescence properties
[EN] The optical and structural properties of CH3NH3PbI3 can be adjusted by introducing other extrinsic ions such as chloride and bromide. In this work, mixed bromide iodide lead perovskites with a 10% fraction of chloride were prepared from methylamine, lead nitrate and the corresponding hydro acid...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2016 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/96943 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/96943 |
| Access Level: | acceso abierto |
| Palabra clave: | Chloride and bromide effect Gap energy tuning Mixed bromide iodide lead perovskites Pawley refinement Photoluminescence Thin film perovskites FISICA APLICADA |
| Sumario: | [EN] The optical and structural properties of CH3NH3PbI3 can be adjusted by introducing other extrinsic ions such as chloride and bromide. In this work, mixed bromide iodide lead perovskites with a 10% fraction of chloride were prepared from methylamine, lead nitrate and the corresponding hydro acid (X = I, Br, Cl). The effect of bromide and chloride incorporation on different properties of perovskite thin film was investigated. The Pawley fit method indicates the formation of the iodide halide MAPbI3 Pm-3 m cubic phase for x = 0 and the tetragonal P4/mmm phase for x ≥ 0.3. All deposited films showed a strong absorbance in the UV vis range. The band gap values were estimated from absorbance measurements. It was found that the onset of the absorption edge for MAPbI2.9-xBrxCl0.1 thin film perovskites ranges between 1.60 and 1.80 eV. Moreover, it was found that both Cl and Br affect the PL emission of the mixed halide lead perovskite, the MAPbI2.9−xBrxCl0.1 films displayed intermediate values from 730 nm (MAPbI2.2Br0.7Cl0.1) to 770 nm (MAPbI2.6Br0.3Cl0.1) |
|---|