Effect of exposure to etidronic acid on the bond strength of calcium silicate-based cements after 1 and 21 days: an in vitro study
Background: After reparation of root perforations with calcium silicate-based cements (CSBC), the surface of the material is expected to be exposed to root canal irrigants (RCI) while resuming the root canal treatment. Methods: The aim of this study was to compare the effect of exposure to a mixture...
| Authors: | , , , |
|---|---|
| Format: | article |
| Publication Date: | 2021 |
| Country: | España |
| Institution: | Universidad Complutense de Madrid (UCM) |
| Repository: | Docta Complutense |
| Language: | English |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/133302 |
| Online Access: | https://hdl.handle.net/20.500.14352/133302 |
| Access Level: | Open access |
| Keyword: | 616.314.018:615.46 Bond strength Calcium silicate cements Etidronic acid Root canal irrigants Setting time Odontología (Odontología) Endodoncia Aparatos y material odontológicos 3213.13 Ortodoncia-Estomatología 3311.03 Instrumentos Para Odontología |
| Summary: | Background: After reparation of root perforations with calcium silicate-based cements (CSBC), the surface of the material is expected to be exposed to root canal irrigants (RCI) while resuming the root canal treatment. Methods: The aim of this study was to compare the effect of exposure to a mixture of sodium hypochlorite (NaOCl) and etidronic acid (HEBP) or other irrigants on the Push Out Bond Strength (POBS) of CSBC after two different setting times. 240 root slices 1 mm thick were obtained from single-rooted human teeth. A 1.4 mm diameter perforation was performed on each slice and filled with Biodentine (BD) or ProRoot MTA (PMTA). After 1 or 21 days they were exposed to 17% ethylenediaminetetraacetic acid, 5.25% NaOCl, a mixture of 5.25% NaOCl and 9% HEBP (NaOCl + HEBP) or saline (n = 15) and submitted to a push-out test. POBS results were analysed with ANOVA and Tukey tests. Results: BD showed higher POBS than PMTA after 1 day (p < .05). After 21 days no differences were found between materials. After 1 day exposure to NaOCl + HEBP resulted in higher POBS, compared to the other irrigants (p < .05). Conclusion: POBS results are influenced by the cement, the setting time and the exposure to irrigants. |
|---|