Microhardness and wear behavior of nanodiamond-reinforced nanocomposites for dental applications
In polymer-based dental composites, wear is a three-body wear system mainly abrasive, because of the food particles and wear products suspended in the oral cavity, which are transferred to the microcavities of the surface of the replacements. Due to this fact, the incorporation of nanodiamond as rei...
| Autores: | , , , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2024 |
| País: | España |
| Institución: | Universidad de Sevilla (US) |
| Repositorio: | idUS. Depósito de Investigación de la Universidad de Sevilla |
| OAI Identifier: | oai:idus.us.es:11441/165720 |
| Acceso en línea: | https://hdl.handle.net/11441/165720 https://doi.org/10.1002/pc.29104 |
| Access Level: | acceso abierto |
| Palabra clave: | Hardness Nanodiamond Photocuring Polymer–matrix composite Wear |
| Sumario: | In polymer-based dental composites, wear is a three-body wear system mainly abrasive, because of the food particles and wear products suspended in the oral cavity, which are transferred to the microcavities of the surface of the replacements. Due to this fact, the incorporation of nanodiamond as reinforcement in these polymer–matrix composites, which promotes the creation of a solid lubricant tribofilm surface could be advantageous. With the reinforcement of nanodiamonds, BisGMA/TEGDMA-based composites increase their microhardness by 95%–420%. A maximum hardness exceeding 65 HV is achieved with a reinforcement of 3.2 wt%. The specific wear rate of neat BisGMA/TEGDMA is near 10−4 mm3/Nm and the Archard's coefficient is 2.6 × 105. The incorporation of a content of 1.6 wt% ND is enough to cause a diminution of ~78% in the friction coefficient and a reduction of the specific wear rate and Archard's coefficient of ~50%. Nevertheless, the addition of relatively high contents reduces the effectiveness of photoinitiation and photocuring, which is related to the scattering and absorption of light radiation by ND. This causes a significant decline in elastic properties starting at 50 μm from the surface. |
|---|