Characterization of Interlaminar Friction during the Forming Processes of High-Performance Thermoplastic Composites
Friction is a pivotal factor influencing wrinkle formation in composite material shaping processes, particularly in novel thermoplastic composites like polyetheretherketone (PEEK) and low-melting polyaryletherketone (LM-PAEK) matrices reinforced with unidirectional carbon fibers. The aerospace secto...
| Autores: | , , |
|---|---|
| Tipo de recurso: | artículo |
| Estado: | Versión publicada |
| Fecha de publicación: | 2024 |
| País: | España |
| Institución: | Varias* (Consorci de Biblioteques Universitáries de Catalunya, Centre de Serveis Científics i Acadèmics de Catalunya) |
| Repositorio: | Recercat. Dipósit de la Recerca de Catalunya |
| OAI Identifier: | oai:recercat.cat:10256/24061 |
| Acceso en línea: | http://hdl.handle.net/10256/24061 |
| Access Level: | acceso abierto |
| Palabra clave: | Compostos termoplàstics Resistència de materials Assaigs de materials Fabricació Thermoplastic composites Strength of materials Materials -- Testing Manufacturing processes |
| Sumario: | Friction is a pivotal factor influencing wrinkle formation in composite material shaping processes, particularly in novel thermoplastic composites like polyetheretherketone (PEEK) and low-melting polyaryletherketone (LM-PAEK) matrices reinforced with unidirectional carbon fibers. The aerospace sector lacks comprehensive data on the behavior of these materials under forming conditions, motivating this study's objective to characterize the interlaminar friction of such high-performance thermoplastic composites across diverse temperatures and forming parameters. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) were employed to analyze the thermomechanical behaviors of PEEK and LM-PAEK. These data guided friction tests covering room-to-forming temperatures. Horizontal pull-out fixed-plies tests were conducted to determine the friction coefficient and shear stress dependency concerning temperature, pressure, and pulling rate. Below the melting point, both materials adhered to Coulomb's law for friction behavior. However, above the melting temperature, PEEK's friction decreased while LM-PAEK's friction increased with rising temperatures. These findings highlight the distinct responses of these materials to temperature variations, pulling rates, and pressures, emphasizing the need for further research on friction characterization around glass transition and melting temperatures to enhance our understanding of this phenomenon. |
|---|