Poly(epsilon-caprolactone)/Graphene oxide composite systems: a comparative study on hydrolytic degradation at extreme pH values
[EN] Polycaprolactone/Graphene oxide (PCL/GO) composites are shown to be promising substrates for tissue engineering as their degradation behavior is a key aspect in this type of application. The present paper studies the effect of different GO contents (0.1, 0.2 and 0.5 wt%) of PCL/GO composites on...
| Autores: | , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2020 |
| País: | España |
| Institución: | Universitat Politècnica de València (UPV) |
| Repositorio: | RiuNet. Repositorio Institucional de la Universitat Politécnica de Valéncia |
| Idioma: | inglés |
| OAI Identifier: | oai:riunet.upv.es:10251/171694 |
| Acceso en línea: | https://riunet.upv.es/handle/10251/171694 |
| Access Level: | acceso abierto |
| Palabra clave: | Polycaprolactone Graphene oxide Nanocomposite Hydrolytic degradation Accelerated degradation MAQUINAS Y MOTORES TERMICOS FISICA APLICADA |
| Sumario: | [EN] Polycaprolactone/Graphene oxide (PCL/GO) composites are shown to be promising substrates for tissue engineering as their degradation behavior is a key aspect in this type of application. The present paper studies the effect of different GO contents (0.1, 0.2 and 0.5 wt%) of PCL/GO composites on accelerated hydrolytic degradation at pH 13 and pH 1. Degradation kinetics at pH 13 is strongly affected by GO content, and speed up at higher percentages. The composite with 0.5 wt% of GO was completely degraded in 72 hours, while degradation at pH 1 presents a different profile and seems to have an induction period that lasts more than 1500 hours. Morphological changes, molecular weight distribution, weight loss, degree of swelling and calorimetric properties were obtained as a function of degradation time. According to the results obtained, the addition of small percentages of GO significantly influences the degradation behavior of the composites acting as degradation modulators. |
|---|