Insights from transient absorption spectroscopy into electron dynamics along the Ga-gradient in Cu(In,Ga)Se2 solar cells
Cu(In,Ga)Se2 solar cells have markedly increased their efficiency over the last decades currently reaching a record power conversion efficiency of 23.3%. Key aspects to this efficiency progress are the engineered bandgap gradient profile across the absorber depth, along with controlled incorporation...
| Autores: | , , , , , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2021 |
| País: | España |
| Institución: | Universidad de Cantabria (UC) |
| Repositorio: | UCrea Repositorio Abierto de la Universidad de Cantabria |
| Idioma: | inglés |
| OAI Identifier: | oai:repositorio.unican.es:10902/29133 |
| Acceso en línea: | https://hdl.handle.net/10902/29133 |
| Access Level: | acceso abierto |
| Palabra clave: | Charge carrier recombination CIGS solar cells Composition gradient Minority carrier mobility Transient absorption spectroscopy |
| Sumario: | Cu(In,Ga)Se2 solar cells have markedly increased their efficiency over the last decades currently reaching a record power conversion efficiency of 23.3%. Key aspects to this efficiency progress are the engineered bandgap gradient profile across the absorber depth, along with controlled incorporation of alkali atoms via post-deposition treatments. Whereas the impact of these treatments on the carrier lifetime has been extensively studied in ungraded Cu(In,Ga)Se2 films, the role of the Ga-gradient on carrier mobility has been less explored. Here, transient absorption spectroscopy (TAS) is utilized to investigate the impact of the Ga-gradient profile on charge carrier dynamics. Minority carriers excited in large Cu(In,Ga)Se2 grains with a [Ga]/([Ga]+[In]) ratio between 0.2–0.5 are found to drift-diffuse across ≈1/3 of the absorber layer to the engineered bandgap minimum within 2 ns, which corresponds to a mobility range of 8.7–58.9 cm2 V−1 s−1. In addition, the recombination times strongly depend on the Ga-content, ranging from 19.1 ns in the energy minimum to 85 ps in the high Ga-content region near the Mo-back contact. An analytical model, as well as drift-diffusion numerical simulations, fully decouple carrier transport and recombination behaviour in this complex composition-graded absorber structure, demonstrating the potential of TAS. |
|---|