Growth and luminescence properties of micro- and nanoneedles in sintered CdSe
Sintering CdSe powder under argon flow at temperatures in the range 800-900 degreesC produces the formation of needles on the sample surface. Bundles of parallel needles of a diameter of about 50 nm give rise to a domain-like appearance in the sample. In addition, rods and needles with a wide range...
| Autores: | , , |
|---|---|
| Tipo de recurso: | artículo |
| Fecha de publicación: | 2004 |
| País: | España |
| Institución: | Universidad Complutense de Madrid (UCM) |
| Repositorio: | Docta Complutense |
| Idioma: | inglés |
| OAI Identifier: | oai:docta.ucm.es:20.500.14352/51139 |
| Acceso en línea: | https://hdl.handle.net/20.500.14352/51139 |
| Access Level: | acceso abierto |
| Palabra clave: | 538.9 Optical-Properties Tin Oxide Nanowires Photoluminescence Nanotubes Cathodoluminescence Nanoribbons Física de materiales |
| Sumario: | Sintering CdSe powder under argon flow at temperatures in the range 800-900 degreesC produces the formation of needles on the sample surface. Bundles of parallel needles of a diameter of about 50 nm give rise to a domain-like appearance in the sample. In addition, rods and needles with a wide range of dimensions up to several microns appear distributed in the surface. The influence of ball milling of the starting powder on the formation of the needles is investigated. Cathodoluminescence in the scanning electron microscope has been used to characterize the sintered samples. |
|---|